Description of Autophoretic®
Performance Characteristics
Performance Comparison
Autophoretic® 900 Coatings

 

 

 

 

Initial Cured Film Performance on ACT Cold Rolled Steel Test Panels
Performance on Production Parts or Other Substrates May Vary

Test

Autophoretic® 800 Series

Autophoretic® 700 Series

Autophoretic® 900 Epoxy

Cathodic Electrocoat

Resin Type

PVDC

Acrylic Epoxy Epoxy

Film Thickness (mils)

0.5-1.0

0.5-1.0 0.6-1.0 0.5-1.0

Pencil Hardness

4-7H

H-2H 2H-3H 2H-3H

Gloss @ 60º

5-10

5-15 40 to 60 @ 20º Varies

T-Bend

0T 2T+ 1T-2T 2T+

Reverse Impact

160/ in-lbs
(0.5-0.7 mils)

40 in-lbs 160 in-lbs (0.5-0.7mils) 40 in-lbs

Cross Hatch Adhesion

No Failure

No Failure

No Failure

No Failure

Humidity (1,000 hours)

No Failure

No Failure

No Failure

No Failure

Water Immersion (240 hours)

No Failure

No Failure

No Failure

No Failure

Neutral Salt Spray

Scribe (3mm Creep)

No Scribe (< 10% rust)

 

600-1000 hrs

2000 hours

 

336-500 hours

1200 hours

 

336-500 hours

1000 hours

 

500->1000 hrs

2000 hours

Cure Temperature

220° F

350°F 365°F 375°F

Temperature Resistance

(Temperature resistance of ACC 800 series is dependent upon duration and air flow conditions. We recommend life cycle testing for parts which will be exposed to operating environments of greater than 200° F)

 

250° F

 

450° F

 

+450°F

 

+450°F

VOC (EPA Reference Method 24) Zero 1.6 lbs/gal < 0.3 lbs/gal  > 0.7 lbs/gal